Aluminum Alloys

Material Overview

-	Al	Si + Fe	Cu	Mn	Fe	Si	Cr	Mg	-	-	-
99%	0.95%	0.05-0.2%	0.05%	...	...	...	....	...	...	...	...
...	...	0.05%	0.01%	0.4%	0.1%	0.01%	....	...	...	...	...
...	...	0.05-0.2%	1-1.5%	0.7%	0.6%	....	....	...	...	...	...
...	...	0.1%	0.1%	0.4%	0.25%	0.15-0.35%	2.2-2.8%	...	...	...	...
...	...	...	0.05-0.2%	0.4%	0.3%	0.05-0.2%	4.5-5.6%	...	...	...	...
...	...	0.1%	0.1%	0.4%	0.25%	0.15-0.35%	3.1-3.9%	...	...	...	...
...	...	...	0.15-0.4%	0.15%	0.7%	0.4-0.8%	0.04-0.35%	0.8-1.2%	...	...	...

Aluminum 1100

UNS A91100

1100 is a non-heat-treatable aluminum alloy. It soft and ductile with excellent workability as the most weldable aluminum alloy. Cold working increases its strength. 1100 exhibits excellent resistance under severely corrosive conditions. Great for use when electrical conductivity is required. This aluminum is often used for decorative architectural trim, screens, grills, cold-headed and cold-threaded parts.

Aluminum 1100 Fact Sheet

Composition	[Al min. 99%, Si + Fe 0.95%, Cu 0.05-0.2%, Mn 0.05%]
Specifications	ASTM B211
Density	0.098 lbs/in³
Tensile Strength	15 Kpsi*
Elongation	10%*
Melt	1220° F
Max. Operating Temperature	400° F (loses tensile strength)

* Tensile strength and elongation are for annealed 0.012″ wire diameter. Please note that material performance data is provided a reference guide only… There are many factors involved in wire cloth performance, so please consult with an experienced engineer before choosing the metal best suited for your unique needs!

Aluminum 1350

UNS A91350

1350 is a non-heat-treatable aluminum alloy. Composed of a minimum 99.5% aluminum. Cold working increases its strength. Often used for electrical conductivity.

Aluminum 1350 Fact Sheet

Composition	[Fe 0.4%, Si 0.1%, Cu 0.05%, Mn 0.01%, Cr 0.01% (max. values)]
Specifications	ASTM B233
Density	.098 lbs/in³
Tensile Strength	18 Kpsi*
Elongation	10%*
Melt	1215° F
Max. Operating Temperature	400° F (loses tensile strength)

Aluminum 3003

UNS A93003

3003 is a non-heat-treatable aluminum alloy. Due to its composition, 3003 is approximately 20% stronger than type 1100. Cold working increases its strength. It is readily worked and contains magnesium for excellent service under severely corrosive conditions.

Aluminum 3003 Fact Sheet

Composition	[Mn 1-1.5%, Fe 0.7%, Si 0.6%, Cu 0.05-0.2%]
Specifications	ASTM B211, AMS-QQ-A-225
Density	.099 lbs/in³
Tensile Strength	25 Kpsi*
Elongation	10%*
Melt	1210° F
Max. Operating Temperature	400° F (loses tensile strength)

Aluminum 5052

UNS A95052

5052 is a non-heat-treatable aluminum alloy known for its durability. Cold working increases its strength. It contains magnesium for excellent service under severely corrosive conditions. 5052 is especially resistant to marine atmosphere and salt water corrosion. Often used for marine and chemical industry application.

Aluminum 5052 Fact Sheet

Composition	[Mg 2.2-2.8%, Fe 0.4%, Cr 0.15-0.35%, Si 0.25%, Cu 0.1%, Mn 0.1%]
Specifications	ASTM B211
Density	.098 lbs/in³
Tensile Strength	28 Kpsi*
Elongation	22%*
Melt	1200° F
Max. Operating Temperature	400° F (loses tensile strength)

Aluminum 5056

UNS A95056

5056 is the strongest non-heat-treatable aluminum alloy. Cold working increases its strength. It contains magnesium for excellent service under severely corrosive conditions. While strong, this aluminum is quite ductile and serves great for wire screens and fasteners.

Aluminum 5056 Fact Sheet

Composition	[Mg 4.5-5.6%, Fe 0.4%, Si 0.3%, Mn 0.05-0.2%, Cr 0.05-0.2%]
Specifications	ASTM B21, AMS 4182
Density	.096 lbs/in³
Tensile Strength	35 Kpsi*
Elongation	26%*
Melt	1180° F
Max. Operating Temperature	400° F (loses tensile strength)

Aluminum 5154

UNS A95154

5154 is a non-heat-treatable aluminum alloy. This aluminum has moderate strength, excellent formability and corrosion resistance. Great for cold heading applications.

Aluminum 5154 Fact Sheet

Composition	[Mg 3.1-3.9%, Fe 0.4%, Cr 0.15-0.35%, Si 0.25%, Cu 0.1%, Mn 0.1%]
Specifications	ASTM B211
Density	.096 lbs/in³
Tensile Strength	35 Kpsi*
Elongation	26%*
Melt	1180° F
Max. Operating Temperature	400° F (loses tensile strength)

Aluminum 6061

UNS A96061

6061 is the most versatile heat-treatable aluminum alloy. It has excellent corrosion resistance, strength, and formability. Often used in a wide variety of mechanical applications such as fasteners, fittings, marine, aircraft, and aerospace uses.

Aluminum 6061 Fact Sheet

Composition	[Mg 0.8-1.2%, Si 0.4-0.8%, Fe 0.7%, Cu 0.15-0.4%, Cr 0.04-0.35%, Mn 0.15%]
Specifications	ASTM B211, AMS QQ-A-225/8
Density	.098 lbs/in³
Tensile Strength	20 Kpsi*
Elongation	26%*
Melt	1200° F
Max. Operating Temperature	400° F (loses tensile strength)

Specification Charts

Alloy / Number	Cr	Ni	C	Mn Max.	Si Max.	P Max.	S. Max.	Other Elements
304 Stainless Steel Mesh	18.0 – 20.0	8.0 – 11.0	0.08 Max	2.0	1.0	0.04	0.03	–
304L Stainless Steel Mesh	18.0 – 20.0	8.0 – 11.0	0.08 Max	2.0	1.0	0.04	0.03	–
309 Stainless Steel Mesh	18.0 – 20.0	8.0 – 11.0	0.08 Max	2.0	1.0	0.04	0.03	–
310 Stainless Steel Mesh	18.0 – 20.0	8.0 – 11.0	0.08 Max	2.0	1.0	0.04	0.03	–
314 Stainless Steel Mesh	18.0 – 20.0	8.0 – 11.0	0.08 Max	2.0	1.0	0.04	0.03	–
316 Stainless Steel Mesh	18.0 – 20.0	8.0 – 11.0	0.08 Max	2.0	1.0	0.04	0.03	–

Previous: Copper, Brass & Bronze Alloys

Next: Silver